POLYOL for car seats and interior molding

HPOP40

20-23

-

≤0.05

6-9

-

≤8000

-

-

Mixed with high activity polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, 

motorcycles, bicycles and steeling wheels. It can increase the bearing capacity of foam products.

High-activity polymer polyol with solid content 40% can be used to produce high resilience slabstock foam, with a better supporting performance. It can be also used to produce molded foam, which has a higher activity, shorter stripping time, better opening effect. It can be used for interior materials. Comparing with POP36/28 and POP93/28, HPOP40 has a better hardening effect and opening effect for foams.

EP-3033

31.5-34.5

≤0.1

≤0.1

5-7

-

-

≤10

≤100

Mixed with polymer polyol grafted polyether together. Used in producing high resilience, 

cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels. 

With a functionality of 4, molecular weight of 7000, and low ordor, this high-activity polyether polyols can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. Comparing with EP-330NY, this product can sustain or even increase the hardness, when increasing the resilience.

This product has a higher functionality and may worsen the hole style of foam in a full MDI or M/T system. Therefore, the user is required to adjust formula according to his own formula system. Because of its higher functionality, there may result in gel formation in the synthesis of polyurethane prepolymer. So it should not used in CASE series.

 EP-330N（G）

32.5-35.5

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

High activity polyether . Mixed with polymer polyol grafted polyether together. Used in producing high resilience, 

cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels. 

With a functionality  of 3, molecular weight of 5000, and low ordor, this kind of high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. It is particularly suitable for the preparation of a variety of automobile interior materials.

EP-330N(Y)

32.5-35.5

≤0.08

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

Comparing with EP-330N(G), this product can minimize the odor.

EP-3600

26.5-29.5

≤0.06

≤0.05

5-7

≤0.08

1000-1600

≤5

≤50

Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, 

bicycles and steering wheels. It can also be used to produce automobile sealant.

With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. Comparing with EP-330NY, EP-3600 can be used to prepare more resilient foam with less hardness. This product can also be used for CASE series, which can effectively improve its tensile strength and resilience.

EP-551C

54.5-57.5

≤0.05

≤0.05

5-7

≤0.05

400-600

≤3

≤50

Mixed with polymer polyol. Used in producing high resilience, thermal-molded foam for cushions of automobiles, motorcycles, bicycles and steering wheels. 

With a functionality of 3 and molecular weight of 3000, this high-activity polyether polyol can be used to produce thermal-molded foams, which has a higher activity, shorter stripping time. Its activity is higher than DEP-5631D, but lower than EP-330NY.

EP-553

54.5-57.5

≤0.05

≤0.05

5-7

≤0.05

400-600

≤3

≤50

Mixed with polymer polyol. Used in producing high resilience, thermal-molded foam for cushions of automobiles, motorcycles, bicycles and steeling wheels. 

With a functionality of 3 and molecular weight of 3000, this high-activity polyether polyol can be used to produce thermal-molded foams, which has a higher activity, shorter stripping time. Its activity is higher than DEP-5631D, but lower than EP-551C.