POLYOL for waterproof materials

DL-400

270-290

≤0.05

≤0.05

5-7

-

60-80

≤5

≤50

This is a low unsaturated polypropylene oxide ether diol, with a molecular weight of 400-8000.  As the basis component for the soft segment structure of polyurethane, it can be used for a variety of polyurethane  waterproof products.

DL series products are mainly used for CASE series products, with a molecular weight range from 700 to 12000. For application, as the molecular weight of the polyol increases, the elongation at break gradually increases while the tensile strength and hardness decreases. 

Users may choose polyether polyols of different molecular weight according to their final product’s request. They can also arrange MN-3050DF, EP-330NG or EP-3600 in groups to increase the product’s tensile strength.

DL-1000D

109-115

≤0.05

≤0.02

5-8

-

120-180

-

-

DL-2000D

54.5-57.5

≤0.05

≤0.02

5-8

≤0.01

270-370

-

-

DL-2500D

43-47

≤0.05

≤0.02

5-8

≤0.01

-

-

-

DL-3000D

36-39

≤0.05

≤0.02

5-8

≤0.01

500-600

-

-

DL-4000D

26.5-29.5

≤0.05

≤0.02

5-8

≤0.01

800-1000

-

-

EDL-8000

12.5-15.5

≤0.08

≤0.05

5-8

  -

≤5000

-

-

MN-3050DF

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

-

-

This is a low unsaturated polypropylene oxide ether triol, with a molecular weight of 3000. It can be used for a variety of  waterproof polyurethane products, effectively improving the tensile strength of the polyurethane products.

It can not be used to prepare flexible polyurethane foam, as it may cause sponge heartburn.

MN-430

360-420

≤0.10

≤0.10

5-7

-

400-700

≤20

-

When used in waterproof polyurethane products, it can increase the product’s hardness.

MN-500

330-350

≤0.08

≤0.05

5-7

-

-

≤5

≤50

MN-700

225-255

≤0.05

≤0.10

5-7

-

200-400

≤5

≤50

MN-1000

163-173

≤0.05

≤0.10

5-7

-

-

≤5

≤50

NRC-2000

54.5-57.5

≤0.05

≤0.05

5-7

-

-

≤10

≤100

With a functionality of 2 and molecular weight of 2000, this high ethylene oxide content polyether polyol can be used to synthesize water-swellable polyurethane for waterproof plugging materials.

NRC-3000

54.5-57.5

≤0.05

≤0.05

5-7

-

-

≤10

≤100

With a functionality of 3 and molecular weight of 3000, this high ethylene oxide content polyether polyols can be used to synthesize water-swellable polyurethane for waterproof plugging materials.